- 熔体流动速率 [g/10min]: 1.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Vinyl Acetate Content | 4.0 % | 4.0 % | |||
| Thickness | 31.8 microns | 1.25 mil | 2:1 BUR; 25 mil die gap | ||
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 340 % | 340 % | ASTM D882 | ||
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 180 g | 180 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 250 g | 250 g | ASTM D1922 | ||
| Dart drop Test | 140 g | 0.309 lb | F50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 21.4 MPa | 3100 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 145 MPa | 21000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 165 MPa | 24000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.0 % | 4.0 % | (NA 340-141 - high slip, medium antiblock); ASTM D1003 | ||
| Gloss | 75 % | 75 % | at 45° (NA 340-141 - high slip, medium antiblock); ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 191 °C | 375 °F | |||
| Descriptive Properties | |||||
| Antiblock | High | ||||
| Slip | Medium | ||||