- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D1558 | ||
| Thickness | 25.4 microns | 1.00 mil | 2:1 BUR; 20 mil die gap | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.3 MPa | 1500 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 11.7 MPa | 1700 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 250 % | 250 % | ASTM D882 | ||
| Film Elongation at Break, TD | 520 % | 520 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 136 g | 136 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 120 g | 120 g | ASTM D1922 | ||
| Dart drop Test | 50.0 - 60.0 g | 0.110 - 0.132 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 23.4 MPa | 3400 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 214 MPa | 31000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 241 MPa | 35000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 5.5 % | 5.5 % | ASTM D1003 | ||
| Gloss | 95 % | 95 % | at 60°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 160 °C | 320 °F | |||
| Descriptive Properties | |||||
| Antiblock | Low | ||||
| Slip | High | ||||