- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ExxonMobil Method |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.25 g/10 min | 0.25 g/10 min | ExxonMobil Method |
| Antiblock Level | 4000 ppm | 4000 ppm | |
| Slip Level | 500 ppm | 500 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.7 MPa | 1550 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.86 MPa | 1430 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 130 % | 130 % | ASTM D882 |
| Film Elongation at Break, TD | 590 % | 590 % | ASTM D882 |
| Film Elongation at Yield, MD | 6.7 % | 6.7 % | ASTM D882 |
| Film Elongation at Yield, TD | 5.0 % | 5.0 % | ASTM D882 |
| Elmendorf Tear Strength MD | 330 g | 330 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 120 g | 120 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 6.50 g/micron | 165 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.36 g/micron | 60.0 g/mil | ASTM D1922 |
| Dart Drop | 3.54 g/micron | 90.0 g/mil | ASTM D1709 |
| Dart drop Test | 180 g | 0.397 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 25.3 MPa | 3670 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.3 MPa | 3530 psi | ASTM D882 |
| 1% Secant Modulus, MD | 186 MPa | 27000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 245 MPa | 35500 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 109 °C | 229 °F | Peak Melting Temperature; ExxonMobil Method |
| Crystallization Temperature | 97.0 °C | 207 °F | ExxonMobil Method |
| Vicat Softening Point | 92.8 °C | 199 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 20.5 % | 20.5 % | ASTM D1003 |
| Gloss | 32 % | 32 % | 45°; ASTM D2457 |