- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | Exxon Method |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 7.40 MPa | 1070 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.40 MPa | 1070 psi | ASTM D882 |
| Film Elongation at Break, MD | 390 % | 390 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Secant Modulus, MD | 0.123 GPa | 17.8 ksi | ASTM D882 |
| Secant Modulus, TD | 0.141 GPa | 20.5 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 160 g | 160 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 420 g | 420 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 7.87 g/micron | 200 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 20.7 g/micron | 525 g/mil | ASTM D1922 |
| Dart Drop | 11.8 g/micron | 300 g/mil | F50; ASTM D1709 |
| Dart drop Test | 240 g | 0.529 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 72.0 MPa | 10400 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 52.0 MPa | 7540 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 115 °C | 239 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 1.3 % | 1.3 % | ASTM D1003 |
| Gloss | 94 % | 94 % | 45°, ASTM D-2457 |