- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.921
- 拉伸强度 [MPa]: 11.0
- 弯曲强度 [MPa]: 9.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Melt Flow | 30 g/10 min | 30 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 375 % | 375 % | ASTM D638 |
| Modulus of Elasticity | 0.276 GPa | 40.0 ksi | Secant; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 93.0 °C | 199 °F | ASTM D1525 |