- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 - 0.922 g/cc | 0.0332 - 0.0333 lb/in³ | TSTM 209 B |
| Melt Flow | 4.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | >= 7.85 MPa | >= 1140 psi | Sheet; ASTM D882 |
| Film Elongation at Break, MD | >= 250 % | >= 250 % | ASTM D882 |
| Elongation at Break | >= 350 % | >= 350 % | Sheet; ASTM D882 |
| Film Tensile Strength at Break, MD | >= 16.67 MPa | >= 2418 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 92.0 - 94.0 °C | 198 - 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 12 % | <= 12 % | ASTM D1003 |
| Gloss | >= 70 % | >= 70 % | At 60°C; ASTM D523 |