- 熔体流动速率 [g/10min]: 22.0
- 密度 [g/cm3]: 0.919
- 缺口冲击强度: 42.0
- 拉伸强度 [MPa]: 8.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Environmental Stress Crack Resistance | 3.0 hour | 3.0 hour | DSM Method |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 190 °C | 22 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 45 | 45 | ISO 868 |
| Ball Indentation Hardness | 16.0 MPa | 2320 psi | ISO 2039-1 |
| Tensile Strength at Break | 7.00 MPa | 1020 psi | ISO 527/2 |
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ISO 527/2 |
| Elongation at Break | 400 % | 400 % | |
| Tensile Modulus | 0.175 GPa | 25.4 ksi | ISO 527/2 |
| Izod Impact, Notched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | ISO 180/A |
| Tensile Creep Modulus, 1 hour | 80.0 MPa | 11600 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 82.0 °C | 180 °F | ISO 306 |
| Heat Distortion Temperature | 39.0 °C | 102 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 105 °C | 221 °F | |