- 熔体流动速率 [g/10min]: 24.0
- 拉伸强度 [MPa]: 10.3
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.916 g/cc | 0.916 g/cc | ASTM D1505 |
| Thickness | 50.0 - 300 microns | 1.97 - 11.8 mil | |
| Melt Flow | 24 g/10 min @Load 2.16 kg, Temperature 190 °C | 24 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 43 | 43 | ASTM D2240 |
| Tensile Strength at Break | 10.5 MPa | 1520 psi | ASTM D638 |
| Tensile Strength, Yield | 10.3 MPa | 1490 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Crystallization Temperature | 104 °C | 219 °F | ASTM D1525 |
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D740 |