- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.916
- 拉伸强度 [MPa]: 12.5
- 弯曲模量 [MPa]: 0.200
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| Melt Flow | 6.0 - 8.0 g/10 min | 6.0 - 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 12.5 MPa | 1810 psi | ASTM D638-64T |
| Elongation at Break | 500 % | 500 % | 50mm/min |
| Flexural Modulus | 0.200 GPa | 29.0 ksi | ASTM D760-66 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 87.0 °C | 189 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |