- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.921
- 拉伸强度 [MPa]: 9.4
- 脆化温度 [℃]: -35.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D792 |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 190 °C | 25 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength at Break | 8.20 MPa | 1190 psi | ASTM D638 |
| Tensile Strength, Yield | 9.40 MPa | 1360 psi | ASTM D638 |
| Elongation at Break | 175 % | 175 % | ASTM D638 |
| Secant Modulus | 0.227 GPa | 32.9 ksi | 2%; ASTM D790 |
| 0.295 GPa | 42.8 ksi | 1%; ASTM D790 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 86.0 °C | 187 °F | ASTM D1525 |
| Brittleness Temperature | <= -35.0 °C | <= -31.0 °F | 0% Failure Rate; ASTM D746 |