- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.955
- 缺口冲击强度: 2.78
- 拉伸强度 [MPa]: 26.9
- 弯曲模量 [MPa]: 1.14
- 热变形温度 [℃]: 70.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D1505 | ||
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 26.9 MPa | 3900 psi | 2 in/min (50 mm/min); ASTM D-638 | ||
| Elongation at Break | 630 % | 630 % | 2 in/min (50 mm/min); ASTM D-638 | ||
| Flexural Modulus | 1.14 GPa | 165 ksi | Tangent Method 1; ASTM D-790 | ||
| Izod Impact, Notched | 2.78 J/cm | 5.21 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 | ||
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| process | Blow Molding | ||||
| region | Europe/Turkey | ||||