- 密度 [g/cm3]: 0.96
- 吸水率 [%]: 0.01
- 拉伸强度 [MPa]: 28.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ISO 1183 |
| Water Absorption | 0.010 % | 0.010 % | immersion |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | after 15 sec.; ISO 868 |
| 66 | 66 | after 3 sec.; ISO 868 | |
| Ball Indentation Hardness | 45.0 MPa | 6530 psi | ISO 2039-1 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 |
| Elongation at Yield | 10 % | 10 % | ISO 527 |
| Tensile Modulus | 1.35 GPa | 196 ksi | ISO 527 |
| Compressive Yield Strength | 9.00 MPa | 1310 psi | at 1% nominal strain; ISO 604 |
| 15.0 MPa | 2180 psi | at 2% nominal strain; ISO 604 | |
| 23.0 MPa | 3340 psi | at 5% nominal strain; ISO 604 | |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 10.5 J/cm² | 50.0 ft-lb/in² | Partial Break; ISO 179/1eA |
| Abrasion | 350 | 350 | Relative loss per DSM internal test (CESTILENE HD 1000 = 100) |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 93 |
| Dielectric Constant | 2.4 @Frequency 100 Hz | 2.4 @Frequency 100 Hz | IEC 250 |
| 2.4 @Frequency 1e+6 Hz | 2.4 @Frequency 1e+6 Hz | IEC 250 | |
| Dielectric Strength | <= 45.0 kV/mm | <= 1140 kV/in | IEC 243 |
| Dissipation Factor | 0.00020 @Frequency 100 Hz | 0.00020 @Frequency 100 Hz | IEC 250 |
| 0.00020 @Frequency 1e+6 Hz | 0.00020 @Frequency 1e+6 Hz | IEC 250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 175 - 225 µm/m-°C @Temperature 20.0 °C | 97.2 - 125 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | |
| Melting Point | 130 - 135 °C | 266 - 275 °F | ISO 3146; DSC, 10°C/min |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | 20,000 hours continuous |
| 120 °C | 248 °F | for short periods | |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO 75 method A |
| Vicat Softening Point | 80.0 °C | 176 °F | ISO 306 |
| Minimum Service Temperature, Air | -100 °C | -148 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| Oxygen Index | <= 20 % | <= 20 % | ISO 4589 |