- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 0.800
- 硬度: 33.0
- 热变形温度 [℃]: 62.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.026 cm/cm | 0.026 in/in | MD; ASTM D955 |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 33 | 33 | ASTM D785 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 350 % | 350 % | ASTM D638 |
| Elongation at Yield | 44 % | 44 % | ASTM D638 |
| Tensile Modulus | 0.9501 GPa | 137.8 ksi | ASTM D638 |
| Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
| Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.2 °C | 144 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.8 °C | 109 °F | |