- 拉伸强度 [MPa]: 15.2
- 弯曲模量 [MPa]: 0.586
- 热变形温度 [℃]: 48.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.01 g/cc | 1.01 g/cc | ASTM D792 | ||
| Melt Index of Compound | 6.5 g/10 min | 6.5 g/10 min | 2.16/190; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | 2"/min; ASTM D638 | ||
| Elongation at Break | 50 % | 50 % | 2"/min; ASTM D638 | ||
| Flexural Modulus | 0.586 GPa | 85.0 ksi | at 1% secant modulus; ASTM D790 | ||
| Impact Test | 20.3 J @Thickness 3.17 mm, Temperature 23.0 °C | 15.0 ft-lb @Thickness 0.125 in, Temperature 73.4 °F | ARM impact | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 | ||
| Flammability, UL94 | V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | |||
| V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | ||||
| Descriptive Properties | |||||
| UV Stabilization | UV-4 | ||||