- 密度 [g/cm3]: 0.945
- 拉伸强度 [MPa]: 13.1
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.945 g/cc | 0.0341 lb/in³ | Compound; ASTM D792 |
Oxidative Induction Time (OIT) | >= 200 min | >= 200 min | At 200°C, Al-pan; ASTM D3895 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Yield | 13.1 MPa | 1900 psi | Expanded Compound; ASTM D638 |
20.0 MPa | 2900 psi | Compound; ASTM D638 | |
Elongation at Break | 500 % | 500 % | Expanded Compound; ASTM D638 |
600 % | 600 % | Compound; ASTM D638 | |
Electrical Properties | Metric | English | Comments |
Dielectric Constant | 2.33 @Frequency 1e+6 Hz | 2.33 @Frequency 1e+6 Hz | ASTM D1531 |
Dissipation Factor | 0.000040 @Frequency 1e+6 Hz | 0.000040 @Frequency 1e+6 Hz | ASTM D1531 |