- 熔体流动速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.955
- 拉伸强度 [MPa]: 23.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ISO 1183 | ||
| Environmental Stress Crack Resistance | 180 hour | 180 hour | Igepal 10%, F50; ASTM D1693-A | ||
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |||
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 10 % | 10 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 0.900 GPa | 131 ksi | 1mm/min; ISO 527-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 190 - 250 °C | 374 - 482 °F | |||
| Mold Temperature | 10.0 - 40.0 °C | 50.0 - 104 °F | |||
| Descriptive Properties | |||||
| Full Notch Creep-Test (hours) | 13 | 6 MPa, 50°C, Arcopal N110 2%, ISO/DIS 16700-2000 | |||
| Injection Velocity | highest possible | ||||