- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.953
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 0.35 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.35 g/10 min @Load 11.0 lb, Temperature 374 °F | ASTM D1238 | ||
| High Load Melt Index | 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 9.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 26.0 MPa | 3770 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 31.0 MPa | 4500 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 684 % | 684 % | ASTM D882 | ||
| Film Elongation at Break, TD | 977 % | 977 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 0.800 g/micron | 20.3 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 8.30 g/micron | 211 g/mil | ASTM D1922 | ||
| Dart Drop | 5.28 g/micron | 134 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 78.0 MPa | 11300 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 61.0 MPa | 8850 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 125 °C | 257 °F | Sealing Initial Temperature; Braskem® Method | ||
| Descriptive Properties | |||||
| Minimum Recommended Thickness | 10 µm | ||||
| Molecular Weight Distribution | Bimodal | ||||
| Puncture Strength | 57 J/m | Braskem® Method | |||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.