- 熔体流动速率 [g/10min]: 0.45
- 密度 [g/cm3]: 0.947
- 缺口冲击强度: 2.4
- 拉伸强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 1080
- 热变形温度 [℃]: 68.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.947 g/cc | 0.0342 lb/in³ | ASTM-D792 |
| ESCR 100% Igepal® | >= 1000 hour @Thickness 2.00 mm, Temperature 50.0 °C | >= 1000 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 0.45 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.45 g/10 min @Load 11.0 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM-D2240 |
| Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM-D638 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ASTM-D638 |
| Elongation at Break | 770 % | 770 % | ASTM-D638 |
| Elongation at Yield | 9.2 % | 9.2 % | ASTM-D638 |
| Flexural Modulus, 1% Secant | 1080 MPa | 157000 psi | ASTM-D790 |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM-D648 |
| Vicat Softening Point | 122 °C @Load 1.02 kg | 252 °F @Load 2.25 lb | ASTM-D1525 |