- 熔体流动速率 [g/10min]: 0.23
- 密度 [g/cm3]: 0.951
- 缺口冲击强度: 3.4
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 1150
- 热变形温度 [℃]: 71.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM-D792 |
| ESCR 100% Igepal® | >= 1000 hour @Thickness 2.00 mm, Temperature 50.0 °C | >= 1000 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 0.23 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.23 g/10 min @Load 11.0 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | ASTM-D2240 |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM-D638 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM-D638 |
| Elongation at Break | 780 % | 780 % | ASTM-D882 |
| Elongation at Yield | 8.4 % | 8.4 % | ASTM-D882 |
| Flexural Modulus, 1% Secant | 1150 MPa | 167000 psi | ASTM-D790 |
| Izod Impact, Notched | 3.40 J/cm | 6.37 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM-D648 |
| Vicat Softening Point | 125 °C @Load 1.02 kg | 257 °F @Load 2.25 lb | ASTM-D1525 |