- 熔体流动速率 [g/10min]: 7.3
- 密度 [g/cm3]: 0.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM-D792 |
| Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 770 % | 770 % | ASTM-D882 |
| Film Elongation at Break, TD | 380 % | 380 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 5.0 g | 5.0 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 10 g | 10 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 0.200 g/micron | 5.08 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 0.400 g/micron | 10.2 g/mil | ASTM-D1922 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 710 MPa | 103000 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 790 MPa | 115000 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 47 % | 47 % | ASTM-D1003 |
| Gloss | 52 % | 52 % | Angle 60°; ASTM-D2457 |