- 熔体流动速率 [g/10min]: 50.0
- 密度 [g/cm3]: 0.956
- 缺口冲击强度: 0.28
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 1190
- 热变形温度 [℃]: 71.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in³ | ASTM-D792 |
| Melt Flow | 50 g/10 min @Load 2.16 kg, Temperature 190 °C | 50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ASTM-D2240 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM-D638 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM-D638 |
| Flexural Modulus, 1% Secant | 1190 MPa | 173000 psi | ASTM-D790 |
| Izod Impact, Notched | 0.280 J/cm | 0.525 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM-D648 |
| Vicat Softening Point | 125 °C @Load 1.02 kg | 257 °F @Load 2.25 lb | ASTM-D1525 |