- 熔体流动速率 [g/10min]: 0.37
- 拉伸强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 1.65
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.963 g/cc | 0.963 g/cc | ASTM D1505 |
| ESCR 100% Igepal® | 15 hour | 15 hour | Condition B, F50; ASTM D1693 |
| Melt Flow | 0.37 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.37 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | 500 % | 500 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 1.65 GPa | 239 ksi | Tangent; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A clamp, Type I Specimen; ASTM D746 |