- 密度 [g/cm3]: 0.955
- 拉伸强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 1.345
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | Condition B; ASTM D 1693 |
| High Load Melt Index | 5.5 g/10 min @Load 21.6 kg, Temperature 190 °C | 5.5 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 Type IV |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 Type IV |
| Flexural Modulus | 1.345 GPa | 195.1 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 210 °C | 379 - 410 °F | stock temperature |