- 熔体流动速率 [g/10min]: 0.34
- 密度 [g/cm3]: 0.949
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 1.07
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 250 hour | 250 hour | Cond. B; ASTM D1693 |
| Melt Flow | 0.34 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.34 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 2 in/min; Type IV bar; ASTM D638 |
| Elongation at Break | 500 % | 500 % | 2 in/min; Type IV bar; ASTM D638 |
| Flexural Modulus | 1.07 GPa | 155 ksi | Tangent; 16:1 span:depth; 0.5 in/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |