- 熔体流动速率 [g/10min]: 0.65
- 密度 [g/cm3]: 0.964
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1.654
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.964 g/cc | 0.0348 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 15 hour | 15 hour | Condition A, F50 100% Igepal CO-630, ASTM D1693; Condition B, F50: 10, ASTM D1693 |
| Melt Flow | 0.65 g/10 min | 0.65 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | 2 in per min; ASTM D638 Type IV |
| Elongation at Break | >= 300 % | >= 300 % | 2 in per min; ASTM D638 Type IV |
| Flexural Modulus | 1.654 GPa | 239.9 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -118 °C | <= -180 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 171 - 226 °C | 340 - 439 °F | |