- 密度 [g/cm3]: 0.945
- 拉伸强度 [MPa]: 22.0
- 弯曲强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 0.900
- 脆化温度 [℃]: -59.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 24 hour @Temperature 50.0 °C | >= 24 hour @Temperature 122 °F | F50, Cond. B.; ASTM D1693 |
| High Load Melt Index | 11 g/10 min @Load 21.6 kg, Temperature 190 °C | 11 g/10 min @Load 47.6 lb, Temperature 374 °F | High Load; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | >= 400 % | >= 400 % | ASTM D638 |
| Flexural Modulus | 0.900 GPa | 131 ksi | 3 pt. secant. ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Brittleness Temperature | <= -59.0 °C | <= -74.2 °F | ASTM D746 |