- 熔体流动速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.962
- 弯曲模量 [MPa]: 1.10
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | ASTM D1505 |
| Melt Flow | 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.5 g/10 min @Load 4.76 lb, Temperature 374 °F | Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 29.0 MPa | 4200 psi | ASTM D638 |
| Elongation at Break | 1200 % | 1200 % | ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Tensile Impact Strength | 174 kJ/m² | 83.0 ft-lb/in² | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 129 °C | 264 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 |