- 熔体流动速率 [g/10min]: 0.67
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 0.758
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | 200 hour | 200 hour | F50, Condition A, ASTM D1693 |
| Melt Flow | 0.67 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.67 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64.6 | 64.6 | ASTM D2240 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Flexural Modulus | 0.758 GPa | 110 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 - 205 °C | 320 - 401 °F | |