- 熔体流动速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.936
- 拉伸强度 [MPa]: 15.0
- 弯曲强度 [MPa]: 45.0
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.580 g/cc | 0.0210 lb/in³ | |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F0, ASTM D1693 |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ASTM D2240 |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Fisher-Johns |
| Vicat Softening Point | 111 °C | 232 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 205 °C | 401 °F | |