- 熔体流动速率 [g/10min]: 5.5
- 缺口冲击强度: 1.1
- 拉伸强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 1.35
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.956 g/cc | 0.956 g/cc | ISO 1183 |
| Melt Flow | 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 14 g/10 min @Load 5.00 kg, Temperature 190 °C | 14 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ISO 868/A |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527 |
| Elongation at Break | 550 % | 550 % | ISO 527 |
| Flexural Modulus | 1.35 GPa | 196 ksi | ISO 178 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ISO 180/A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 135 °C | 275 °F | Internal method |
| Vicat Softening Point | 127 °C @Load 1.00 kg | 261 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |