- 熔体流动速率 [g/10min]: 0.15
- 密度 [g/cm3]: 0.955
- 拉伸强度 [MPa]: 19.3
- 弯曲模量 [MPa]: 0.758
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Condition A - 10% Igepal®; ASTM D1693 |
| Absorption Coefficient | 440 | 440 | ASTM D3349 |
| Carbon Black Loading | 2.6 % | 2.6 % | |
| Melt Flow | 0.15 g/10 min | 0.15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength at Break | 31.7 MPa | 4600 psi | ASTM D638 |
| Tensile Strength, Yield | 19.3 MPa | 2800 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | ASTM D638 |
| Flexural Modulus | 0.758 GPa | 110 ksi | 1% Secant; ASTM D780 |
| 1% Secant Modulus | 531 MPa | 77000 psi | ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.5 @Frequency 1e+6 Hz | 2.5 @Frequency 1e+6 Hz | ASTM D1531 |
| Dielectric Strength | 21.7 kV/mm | 550 kV/in | ASTM D149 |
| Dissipation Factor | 0.00020 @Frequency 1e+6 Hz | 0.00020 @Frequency 1e+6 Hz | ASTM D1531 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 150 µm/m-°C @Temperature 20.0 °C | 83.3 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 149 - 163 °C | 300 - 325 °F | |
| Zone 2 | 177 - 204 °C | 350 - 400 °F | |
| Zone 3 | 191 - 204 °C | 375 - 400 °F | |
| Zone 4-x | 238 - 260 °C | 460 - 500 °F | |
| Adapter Temperature | 246 - 260 °C | 475 - 500 °F | |
| Die Temperature | 246 - 260 °C | 475 - 500 °F | |
| Melt Temperature | 246 - 260 °C | 475 - 500 °F | |