- 熔体流动速率 [g/10min]: 5.7
- 密度 [g/cm3]: 0.957
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.957 g/cc | 0.0346 lb/in³ | ASTM D1505 |
| Water Vapor Transmission | 4.30 g/m²/day | 0.277 g/100 in²/day | 100% Humidity; ASTM F372 |
| Thickness | 50.8 microns | 2.00 mil | 2:1 BUR |
| Melt Flow | 5.7 g/10 min | 5.7 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 21.7 MPa | 3150 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 23.2 MPa | 3360 psi | ASTM D882 |
| Film Elongation at Break, MD | 610 % | 610 % | ASTM D882 |
| Film Elongation at Break, TD | 710 % | 710 % | ASTM D882 |
| Film Elongation at Yield, MD | 4.0 % | 4.0 % | ASTM D882 |
| Film Elongation at Yield, TD | 2.0 % | 2.0 % | ASTM D882 |
| Elmendorf Tear Strength MD | 60 g | 60 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 110 g | 110 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 24.1 MPa | 3500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.4 MPa | 3100 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |