- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 24.1 MPa | 3500 psi | ASTM D822 |
| Film Tensile Strength at Yield, TD | 25.5 MPa | 3700 psi | ASTM D822 |
| Film Elongation at Break, MD | 850 % | 850 % | ASTM D822 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D822 |
| 1% Secant Modulus, MD | 793 MPa | 115000 psi | ASTM D822 |
| 1% Secant Modulus, TD | 1030 MPa | 150000 psi | ASTM D822 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 °C | 390 °F | Typical Extrusion |