- 熔体流动速率 [g/10min]: 19.5
- 密度 [g/cm3]: 0.946
- 缺口冲击强度: 0.443
- 拉伸强度 [MPa]: 23.6
- 弯曲模量 [MPa]: 0.7936
- 热变形温度 [℃]: 64.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.593 - 0.625 g/cc | 0.0214 - 0.0226 lb/in³ | ASTM D1895 |
| Density | 0.946 g/cc | 0.0342 lb/in³ | ASTM D1505 |
| Melt Flow | 19.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 19.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 30.5 cm | 12.0 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength at Break | 13.0 MPa | 1880 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 23.6 MPa | 3420 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 130 % | 130 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 10 % | 10 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.8984 GPa | 130.3 ksi | 1% Secant; 50mm/min; ASTM D638 |
| 1.140 GPa | 165.3 ksi | 50mm/min; ASTM D638 | |
| Flexural Modulus | 0.7936 GPa | 115.1 ksi | 2% Secant; 12.5 mm/min; ASTM D790 |
| 0.9398 GPa | 136.3 ksi | 1% Secant; 12.5 mm/min; ASTM D790 | |
| 1.085 GPa | 157.4 ksi | 12.5 mm/min; ASTM D790 | |
| Izod Impact, Notched | 0.443 J/cm | 0.830 ft-lb/in | ASTM D256 |
| NB @Temperature -18.0 °C | NB @Temperature -0.400 °F | ASTM D4812 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126.3 °C | 259.3 °F | ASTM D3418 |
| Crystallization Temperature | 112.4 °C | 234.3 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 232 °C | 450 °F | |
| Middle Barrel Temperature | 243 °C | 470 °F | |
| Front Barrel Temperature | 246 °C | 475 °F | |
| Nozzle Temperature | 246 °C | 475 °F | |