- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.952
- 缺口冲击强度: 0.379
- 拉伸强度 [MPa]: 26.1
- 弯曲模量 [MPa]: 1.25
- 热变形温度 [℃]: 72.8
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.529 - 0.593 g/cc | 0.0191 - 0.0214 lb/in³ | ASTM D1895 |
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Melt Flow | 20.0 g/10 min @Load 0.980 kg, Temperature 190 °C | 20.0 g/10 min @Load 2.16 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 29.5 cm | 11.6 in | Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 76.0 | 76.0 | ASTM D2240 |
| Tensile Strength, Yield | 26.1 MPa | 3790 psi | 50 mm/min, Type IV; ASTM D4796 |
| Elongation at Yield | 11.0 % | 11.0 % | 50 mm/min, Type IV; ASTM D638 |
| Tensile Modulus | 1.00 GPa | 145 ksi | 1% Secant, 50mm/min; ASTM D638 |
| 1.26 GPa | 183 ksi | 50 mm/min; ASTM D638 | |
| Flexural Modulus | 1.25 GPa | 181 ksi | ASTM D790 |
| 1% Secant Modulus | 1080 MPa | 157000 psi | 12.5mm/min; ASTM D790 |
| 2% Secant Modulus | 0.903 GPa | 131 ksi | 12.5mm/min; ASTM D790 |
| Izod Impact, Notched | 0.379 J/cm @Temperature 23.0 °C | 0.710 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Izod Impact, Unnotched | NB @Temperature -18.0 °C | NB @Temperature -0.400 °F | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 130.2 °C | 266.4 °F | ASTM D3418 |
| Crystallization Temperature | 115.4 °C | 239.7 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.8 °C | 163 °F | ASTM D648 |
| Vicat Softening Point | 124 °C | 256 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 232 °C | 450 °F | |
| Middle Barrel Temperature | 243 °C | 470 °F | |
| Front Barrel Temperature | 246 °C | 475 °F | |
| Nozzle Temperature | 246 °C | 475 °F | |
| Compliance Properties | Metric | English | Comments |
| FDA | Yes | Yes | |