- 熔体流动速率 [g/10min]: 1.7
- 密度 [g/cm3]: 0.945
- 拉伸强度 [MPa]: 28.3
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D4883 |
| Apparent Bulk Density | 0.480 g/cc | 0.0173 lb/in³ | ASTM D1895 |
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | 190 / 21.6 (HLMI); ASTM D1238 |
| <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C | <= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
| Elongation at Break | 910 % | 910 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 131 °C | 268 °F | ASTM D1525 |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |