- 熔体流动速率 [g/10min]: 0.45
- 密度 [g/cm3]: 0.958
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | Exxon Method |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.45 g/10 min | 0.45 g/10 min | Exxon Method (I2). HLMI (I21) is 30 g/10 min. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 32.0 MPa | 4640 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 26.0 MPa | 3770 psi | ASTM D882 |
| Elongation at Break | 410 % | 410 % | ASTM D638 |
| Secant Modulus, MD | 1.15 GPa | 167 ksi | ASTM D882 |
| Secant Modulus, TD | 1.70 GPa | 247 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.433 g/micron | 11.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 28.0 g/micron | 710 g/mil | ASTM D1922 |
| Dart Drop | <= 1.46 g/micron | <= 37.0 g/mil | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 72.0 MPa | 10400 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 36.0 MPa | 5220 psi | ASTM D882 |