- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.962
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | ASTM D 792 |
| Water Vapor Transmission | 6.20 g/m²/day | 0.399 g/100 in²/day | 100°F; E 96/66 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg | 5.0 g/10 min @Load 4.76 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 850 % | 850 % | ASTM D 882 A |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D 882 |
| Secant Modulus, MD | 0.689 GPa | 99.9 ksi | ASTM D 882 A |
| Secant Modulus, TD | 0.703 GPa | 102 ksi | ASTM D 882 A |
| Film Tensile Strength at Break, MD | >= 24.1 MPa | >= 3500 psi | ASTM D 882 A |
| Film Tensile Strength at Break, TD | >= 26.2 MPa | >= 3800 psi | ASTM D 882 A |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D 746 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % | 8.0 % | ASTM D 1003 |
| Gloss | 75 % | 75 % | ASTM D 523 |