- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.955
- 拉伸强度 [MPa]: 27.6
- 弯曲模量 [MPa]: 1.38
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D 792 |
| Environmental Stress Crack Resistance | 35 hour | 35 hour | ASTM D1693 cond. B 10% lgepal |
| 50 hour | 50 hour | ASTM D1693 cond. B 100% lgepal | |
| Melt Flow | 0.35 g/10 min @Load 2.16 kg | 0.35 g/10 min @Load 4.76 lb | ASTM D 1238 |
| High Load Melt Index | 30 g/10 min @Load 21.6 kg | 30 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D 638 type IV |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D 638 type IV |
| Flexural Modulus | 1.38 GPa | 200 ksi | ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 264 °F | ASTM D3417 |