- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.954
- 缺口冲击强度: 1.96
- 拉伸强度 [MPa]: 25.5
- 弯曲强度 [MPa]: 38.2
- 弯曲模量 [MPa]: 0.785
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 30 hour | 30 hour | ASTM D1693 |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Ultimate | 38.2 MPa | 5550 psi | ASTM D638 |
| Tensile Strength, Yield | 25.5 MPa | 3700 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 0.785 GPa | 114 ksi | Olsen Stiffness; ASTM D747 |
| Izod Impact, Notched | 1.96 J/cm | 3.67 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131 °C | 268 °F | ASTM D2117 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |