- 密度 [g/cm3]: 1.5
- 缺口冲击强度: 3.74
- 弯曲模量 [MPa]: 11.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 | ||
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 91.0 MPa | 13200 psi | 5mm/min; ISO 527-2/1A | ||
| 113 MPa | 16400 psi | ASTM D638 | |||
| 49.0 MPa @Temperature 93.3 °C | 7100 psi @Temperature 200 °F | ASTM D638 | |||
| 161 MPa @Temperature -40.0 °C | 23400 psi @Temperature -40.0 °F | ASTM D638 | |||
| Elongation at Break | 1.38 % | 1.38 % | 5mm/min; ISO 527-2/1A | ||
| 1.50 % @Temperature 22.8 °C | 1.50 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 10.5 GPa | 1520 ksi | 1mm/min; ISO 527-2/1A | ||
| 7.17 GPa @Temperature 93.3 °C | 1040 ksi @Temperature 200 °F | ASTM D638 | |||
| 13.6 GPa @Temperature 22.8 °C | 1970 ksi @Temperature 73.0 °F | ASTM D638 | |||
| 15.2 GPa @Temperature -40.0 °C | 2210 ksi @Temperature -40.0 °F | ASTM D638 | |||
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 | ||
| 178 MPa | 25800 psi | ASTM D790 | |||
| 61.4 MPa @Temperature 93.3 °C | 8900 psi @Temperature 200 °F | ASTM D790 | |||
| 215 MPa @Temperature -40.0 °C | 31200 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 11.7 GPa | 1700 ksi | ISO 178 | ||
| 5.70 GPa @Temperature 93.3 °C | 827 ksi @Temperature 200 °F | ASTM D790 | |||
| 10.9 GPa @Temperature 22.8 °C | 1580 ksi @Temperature 73.0 °F | ASTM D790 | |||
| 14.1 GPa @Temperature -40.0 °C | 2040 ksi @Temperature -40.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 3.74 J/cm | 7.00 ft-lb/in | ASTM D256 | ||
| 2.14 J/cm @Temperature 93.3 °C | 4.00 ft-lb/in @Temperature 200 °F | ASTM D256 | |||
| 4.59 J/cm @Temperature -40.0 °C | 8.60 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |||
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Cavity temperature | ||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 200 - 210 °C | 392 - 410 °F | |||
| Zone 2 | 210 - 220 °C | 410 - 428 °F | |||
| Zone 3 | 220 - 230 °C | 428 - 446 °F | |||
| Zone 4 | 230 - 240 °C | 446 - 464 °F | |||
| Die Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Melt Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Drying Temperature | 90.0 - 100 °C | 194 - 212 °F | |||
| Dry Time | 2.00 hour | 2.00 hour | |||
| Moisture Content | 0.200 % | 0.200 % | Necessary low maximum residual | ||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Longer pre-drying times/storage | Can be stored in standard conditions until processed. | ||||
| Pre-drying | Drying is not normally required with proper storage | ||||