- 熔体流动速率 [g/10min]: 1.7
- 密度 [g/cm3]: 0.932
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 14.4
- 弯曲强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.490
- 热变形温度 [℃]: 47.0
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 - 0.947 g/cc | 0.0337 - 0.0342 lb/in³ | Average value: 0.937 g/cc Grade Count:35 |
| Environmental Stress Crack Resistance | 4.00 - 1000 hour | 4.00 - 1000 hour | Average value: 437 hour Grade Count:29 |
| >= 1000 hour @Temperature 50.0 - 50.0 °C | >= 1000 hour @Temperature 122 - 122 °F | Average value: 1000 hour Grade Count:2 | |
| Melt Flow | 1.70 - 135 g/10 min | 1.70 - 135 g/10 min | Average value: 8.33 g/10 min Grade Count:34 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55.0 - 69.0 | 55.0 - 69.0 | Average value: 59.3 Grade Count:10 |
| Tensile Strength, Ultimate | 11.0 - 39.0 MPa | 1600 - 5660 psi | Average value: 24.5 MPa Grade Count:9 |
| Tensile Strength, Yield | 14.4 - 22.1 MPa | 2090 - 3200 psi | Average value: 18.8 MPa Grade Count:33 |
| Elongation at Break | 580 - 1500 % | 580 - 1500 % | Average value: 990 % Grade Count:18 |
| Elongation at Yield | 11.0 - 17.4 % | 11.0 - 17.4 % | Average value: 13.2 % Grade Count:9 |
| Flexural Modulus | 0.490 - 0.892 GPa | 71.0 - 129 ksi | Average value: 0.632 GPa Grade Count:33 |
| Izod Impact, Notched | 0.530 - 5.30 J/cm | 0.993 - 9.93 ft-lb/in | Average value: 2.12 J/cm Grade Count:5 |
| Charpy Impact, Notched | 1.80 - 15.0 J/cm² | 8.57 - 71.4 ft-lb/in² | Average value: 6.27 J/cm² Grade Count:3 |
| >= 15.0 J/cm² @Temperature -30.0 - -30.0 °C | >= 71.4 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 15.0 J/cm² Grade Count:1 | |
| Tensile Impact Strength | 145 - 163 kJ/m² | 69.0 - 77.6 ft-lb/in² | Average value: 154 kJ/m² Grade Count:4 |
| Dart drop Total Energy | 200 - 210 J/cm | 0.375 - 0.393 ft-lb/mil | Average value: 208 J/cm Grade Count:13 |
| Dart Drop | 142 - 152 g/micron | 3610 - 3860 g/mil | Average value: 151 g/micron Grade Count:13 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 - 129 °C | 253 - 264 °F | Average value: 127 °C Grade Count:8 |
| Crystallization Temperature | 112 - 114 °C | 234 - 237 °F | Average value: 113 °C Grade Count:4 |
| Deflection Temperature at 0.46 MPa (66 psi) | 47.0 - 76.0 °C | 117 - 169 °F | Average value: 64.0 °C Grade Count:21 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.3 - 42.0 °C | 99.1 - 108 °F | Average value: 40.4 °C Grade Count:3 |
| Vicat Softening Point | 108 - 122 °C | 226 - 252 °F | Average value: 116 °C Grade Count:16 |
| Brittleness Temperature | -75.0 - -70.0 °C | -103 - -94.0 °F | Average value: -70.4 °C Grade Count:14 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 131 - 315 °C | 268 - 599 °F | Average value: 208 °C Grade Count:13 |