- 熔体流动速率 [g/10min]: 0.72
- 密度 [g/cm3]: 0.934
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in³ | ASTM D792 |
| Melt Flow | 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.72 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 15.0 MPa | 2180 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 |
| Film Elongation at Break, TD | 820 % | 820 % | ASTM D882 |
| Secant Modulus, MD | 0.400 GPa | 58.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.500 GPa | 72.5 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.50 | >= 0.50 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 4.00 g/micron | 102 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 14.0 g/micron | 356 g/mil | ASTM D1922 |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 39.0 MPa | 5660 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 230 °C | 428 - 446 °F | |