- 熔体流动速率 [g/10min]: 0.32
- 密度 [g/cm3]: 0.939
- 吸水率 [%]: 0.01
- 拉伸强度 [MPa]: 18.0
- 弯曲强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 0.590
- 脆化温度 [℃]: -100.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.939 g/cc | 0.0339 lb/in³ | Base Density |
Water Absorption | 0.010 % | 0.010 % | ASTM D570 |
Environmental Stress Crack Resistance | 1000 hour | 1000 hour | |
Melt Flow | 0.32 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.32 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 60 | 60 | ASTM D2240 |
Tensile Strength, Ultimate | 26.0 MPa | 3770 psi | ASTM D638 |
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
Elongation at Break | 800 % | 800 % | ASTM D638 |
Flexural Modulus | 0.590 GPa | 85.6 ksi | ASTM D790 |
Thermal Properties | Metric | English | Comments |
Melting Point | 128 °C | 262 °F | ASTM D3417 |
Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D696 |