- 熔体流动速率 [g/10min]: 1.2
- 密度 [g/cm3]: 0.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 1.2 g/10 min | 1.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 400 % | 400 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Dart drop Test | 60.0 g | 0.132 lb | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 24.8 MPa | 3600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.1 MPa | 3200 psi | ASTM D882 |
| 1% Secant Modulus, MD | 331 MPa | 48000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 379 MPa | 55000 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 90 % | 90 % | at 60°; ASTM D2457 |