- 熔体流动速率 [g/10min]: 2.2
- 密度 [g/cm3]: 0.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 14.0 MPa | 2030 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 16.0 MPa | 2320 psi | ASTM D882 |
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Secant Modulus, MD | 0.280 GPa | 40.6 ksi | ASTM D882 |
| Secant Modulus, TD | 0.330 GPa | 47.9 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 125 g | 125 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 3.94 g/micron | 100 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.72 g/micron | 120 g/mil | ASTM D1922 |
| Dart Drop | 1.89 g/micron | 48.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 60.0 g | 0.132 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 116 °C | 241 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 6.5 % | 6.5 % | ASTM D1003 |
| Gloss | 65 % | 65 % | 45°, ASTM D-2457 |