- 密度 [g/cm3]: 0.94
- 拉伸强度 [MPa]: 20.2992
- 弯曲模量 [MPa]: 0.74994
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 5.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength, Yield | 20.2992 MPa | 2944.15 psi | 2"/min; ASTM D638 |
| Elongation at Break | 360 % | 360 % | 2"/min; ASTM D638 |
| Flexural Modulus | 0.74994 GPa | 108.77 ksi | ASTM D790 |
| Impact | 22.5 @Temperature -20.0 °C | 22.5 @Temperature -4.00 °F | J/mm, instrumented impact, rotomolded test sample; ICO R&D1.14 |