- 熔体流动速率 [g/10min]: 85.0
- 密度 [g/cm3]: 0.93
- 拉伸强度 [MPa]: 15.2
- 弯曲模量 [MPa]: 526
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D 792 |
| Melt Flow | 85 g/10 min @Load 2.16 kg, Temperature 190 °C | 85 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D 2240 |
| Tensile Strength at Break | 9.20 MPa | 1330 psi | Rate of 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | Rate of 50 mm/min; ASTM D 638 |
| Elongation at Break | 104 % | 104 % | Rate of 50 mm/min; ASTM D 638 |
| Elongation at Yield | 12 % | 12 % | Rate of 50 mm/min; ASTM D 638 |
| Tensile Modulus | 0.618 GPa | 89.6 ksi | 1% Secant; ASTM D 638 |
| Flexural Modulus, 1% Secant | 526 MPa | 76300 psi | ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 101 °C | 214 °F | ASTM 1525 |