- 透光率 [%]: 73.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Vapor Transmission | 9.00 g/m²/day | 0.580 g/100 in²/day | at 100°F, 90% RH; ASTM F1249-90 | ||
| Oxygen Transmission | 0.512 cc-mm/m²-24hr-atm | 1.30 cc-mil/100 in²-24hr-atm | 10% RH; ASTM D3985 | ||
| Thickness | 15.2 microns | 0.600 mil | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 75 % | 75 % | ASTM D882 | ||
| Film Elongation at Break, TD | 55 % | 55 % | ASTM D882 | ||
| Secant Modulus, MD | 0.689476 GPa | 100.002 ksi | 2% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.620528 GPa | 90.0014 ksi | 2% Secant; ASTM D882 | ||
| Film Tensile Strength at Break, MD | 75.8 MPa | 11000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 124 MPa | 18000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Shrinkage, MD | 16 % | 16 % | Unrestrained, 100°C Air; ASTM D1204 | ||
| Shrinkage, TD | 9.0 % | 9.0 % | Unrestrained, 100°C Air; ASTM D1204 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.0 % | 1.0 % | ASTM D1003 | ||
| Gloss | 115 % | 115 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 73 % | 73 % | Clarity; ASTM D1746 | ||
| Descriptive Properties | |||||
| Block Force g | 114 | ASTM D3354-89, unconditioned | |||
| Cling g | 65 | ASTM D4649-87, unstretched | |||
| Yield in2/lb | 27000 | Calculated | |||