- 透光率 [%]: 73.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Vapor Transmission | 1.94 g/m²/day | 0.125 g/100 in²/day | at 100°F, 90% RH; ASTM F1249-90 | ||
| Oxygen Transmission | 0.571 cc-mm/m²-24hr-atm | 1.45 cc-mil/100 in²-24hr-atm | 10% RH; ASTM D3985 | ||
| Thickness | 50.8 microns | 2.00 mil | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 95 % | 95 % | ASTM D882 | ||
| Film Elongation at Break, TD | 80 % | 80 % | ASTM D882 | ||
| Secant Modulus, MD | 0.689476 GPa | 100.002 ksi | 2% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.613633 GPa | 89.0014 ksi | 2% Secant; ASTM D882 | ||
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | Film to Metal; ASTM D1894 | ||
| Film Tensile Strength at Break, MD | 110 MPa | 16000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 131 MPa | 19000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Shrinkage, MD | 8.0 % | 8.0 % | 10 min at 100°C Air, unrestrained; ASTM D1204 | ||
| Shrinkage, TD | 4.0 % | 4.0 % | 10 min at 100°C Air, unrestrained; ASTM D1204 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.0 % | 3.0 % | ASTM D1003 | ||
| Gloss | 105 % | 105 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 73 % | 73 % | Clarity; ASTM D1746 | ||
| Descriptive Properties | |||||
| Yield in2/lb | 8100 | Calculated | |||